Gen Industrial / Epoxy Primers / 603 Genepox Zinc Rich Primer
EPOXY PRIMERS · ZINC-RICH PRIMER
603
Genepox Zinc Rich Primer
2K · Epoxy · Zinc-rich
Two-component epoxy primer with pure micronised zinc dust providing cathodic protection.
A two-component, epoxy-based anticorrosive primer containing pure micronised zinc dust and providing cathodic protection. The galvanic action of zinc actively protects the steel and forms the foundation of long-lasting protective systems in highly corrosive environments.
Technical Data
LIGANTE
Epoxy resin, pure zinc dust
COMPONENTES
Two-component (2K)
POSICIÓN EN EL SISTEMA
Zinc-rich primer
DENSIDAD
2.10 ± 0.1 kg/L
SÓLIDOS EN VOLUMEN
52% ± 3
RENDIMIENTO TEÓRICO
5 m²/kg (single coat)
PROPORCIÓN DE MEZCLA
9 : 1 by weight (A : B)
DILUCIÓN
016 Gen Epoxy Thinner
MÉTODO DE APLICACIÓN
Spray
PREPARACIÓN DE SUPERFICIE
Sa 2½ (ISO 8501-1)
RENDIMIENTO
—
RENDIMIENTO
—
SECADO
—
ENVASE
20 kg kit (18 kg A + 2 kg B)
COLOR
Zinc grey
DOCUMENTOS TÉCNICOS
Uso y aplicación
USOS
Used for priming steel and in areas requiring high corrosion resistance, in the structural steel industry and on other steel surfaces. Suitable for steel exposed to water, seawater, chemicals and abrasion.
PREPARACIÓN DE SUPERFICIE Y APLICACIÓN
The surface to be painted must be free from oil, dirt, dust and moisture. Metal surfaces must be abrasive blast-cleaned to at least Sa 2½ according to ISO 8501-1 and primed within 6 hours of blasting. The surface must be rough for good adhesion. Stir components A and B separately, combine them at the specified ratio and mix with a mechanical mixer until homogeneous. Surface temperature must be at least 3 °C above the dew point; do not apply on wet or damp surfaces. Stir the mix regularly during application to keep the zinc pigment from settling.
SECTORES DE USO
→ Steel Structures and Structural Steel
→ Storage Tanks, Pressure Vessels and LPG Cylinders
→ Petrochemical, Refinery and Chemical Plants
→ Ports, Shipyards and Coastal Structures
Technical data are average values at 20 °C and 65% relative humidity. Coverage varies with surface roughness, application method and film thickness. Consult the Gen Boya technical team for project-specific system design.
CARACTERÍSTICAS PRINCIPALES
— Cathodic protection with pure micronised zinc
— High performance in highly corrosive environments
— Ideal for structural steel and coastal structures
— System compatibility with epoxy intermediate coats and polyurethane topcoats
SISTEMA RECOMENDADO
CAPAS SIGUIENTES
Over a 625 Genepox HB Fast or 671 Genepox Masticoat intermediate coat, complete with 773 Genpoly Acr Topcoat or 791 Genpur Topcoat.