Gen Yacht / Underwater Primers and Barrier Systems / Nº 402 Osmo Shield
UNDERWATER PRIMERS AND BARRIER SYSTEMS · BARRIER / PRIMER
402
Osmo Shield
Epoxy · Osmosis barrier · GRP
Epoxy-based, water-resistant barrier coating that minimises water ingress and protects GRP hulls against osmosis.
An epoxy-based, water-resistant protective barrier coating. By minimising water penetration it provides long-lasting protection against osmosis, especially on GRP surfaces. It is applied preventively on new boats and as a protective barrier on boats after osmosis repair.
Technical Data
СВЯЗУЮЩЕЕ
Epoxy
КОМПОНЕНТЫ
Two-component (2K)
МЕСТО В СИСТЕМЕ
Barrier / primer
ТЕОРЕТИЧЕСКИЙ РАСХОД
8 m²/kg
СПОСОБ НАНЕСЕНИЯ
Brush, roller, spray
КОЛИЧЕСТВО СЛОЁВ
3–5 coats for barrier effect
СОВМЕСТИМЫЕ ПРОДУКТЫ
409, 425, 427, 428
РАСХОД
—
РАСХОД
—
РАСХОД
—
РАСХОД
—
РАСХОД
—
ВЫСЫХАНИЕ
Touch dry 4 h · Launch after min. 8–24 h (20 °C, 65% RH)
УПАКОВКА
—
ЦВЕТ
Grey
ТЕХНИЧЕСКАЯ ДОКУМЕНТАЦИЯ
Применение и нанесение
ОБЛАСТИ ПРИМЕНЕНИЯ
Underwater surfaces of GRP (fibreglass) boats; as a protective coat against osmosis; as a barrier in underwater paint systems.
ПОДГОТОВКА ПОВЕРХНОСТИ И НАНЕСЕНИЕ
Abrade the gelcoat to a matt finish, remove dust and wipe with solvent. On boats after osmosis repair, confirm the laminate is dry by moisture measurement. Apply coat by coat by brush, roller or spray until the required thickness is reached. Air and surface temperature must be above +5 °C and relative humidity below 85%; surface temperature must be at least 3 °C above the dew point.
ПОДХОДЯЩИЕ ТИПЫ СУДОВ
Technical data are average values at 20 °C and 65% relative humidity. Coverage varies with surface roughness, application method and film thickness. Consult the Gen Boya technical team for a paint schedule tailored to your boat.
КЛЮЧЕВЫЕ ПРЕИМУЩЕСТВА
— High water resistance
— Osmosis-preventing barrier
— Sound base for antifouling systems
— Epoxy durability
РЕКОМЕНДАЦИЯ ПО СИСТЕМЕ
ПОСЛЕДУЮЩИЕ СЛОИ
409 Vinyl Tie Coat + Gen Antifouling (425, 427, 428)